@article {793,
	title = {The effect of Ni2+ on zinc phosphating of 2024-T3 Al alloy},
	journal = {Surface \& Coatings Technology},
	volume = {187},
	number = {2-3},
	year = {2004},
	note = {ISI Document Delivery No.: 860VHTimes Cited: 27Cited Reference Count: 32},
	month = {Oct},
	pages = {208-215},
	type = {Article},
	abstract = {Zinc phosphate (ZPO) conversion coatings formed on 2024-T3 aluminum alloy, and on high-purity aluminum, after dipping in coating baths containing different amounts of Ni2+, have been studied by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, scanning Auger microscopy (SAM) and electrochemical measurements. Significant variations are observed in coating morphology and in stability against corrosion for the 2024-Al alloy as the amount of Ni2+ in the coating solution increases through the 0-2000 ppm range. By contrast, for high-purity Al, the most marked changes in coating morphology occur only as the Ni2+ concentration reaches 2000 ppm. The presence of additional elements, and especially Cu, in the 2024-Al samples results in an increase in the number of cathodic sites and hence more coating is formed for corresponding conditions. Additionally, the existence of second-phase particles in the 2024-Al sample leads to variations in the coatings at the microstructural level across the surface. These differences include local variations in the amount of Ni2+ in the coatings, as well as the local coverage. (C) 2004 Elsevier B.V. All rights reserved.},
	keywords = {aluminum alloy, ALUMINUM-ALLOY, Auger electron spectroscopy, chemical conversion, CHROMATE CONVERSION COATINGS, CORROSION PROTECTION, FILMS, Ni2+ additive, NICKEL, phosphating, photoelectron spectroscopy, STEEL, SURFACE, XPS},
	isbn = {0257-8972},
	url = {<Go to ISI>://000224371300011},
	author = {Akhtar, A. S. and Susac, D. and Glaze, P. and Wong, K. C. and Wong, P. C. and Mitchell, K. A. R.}
}